烧结钐钴磁体

1:5型和2:17型烧结Sa钴磁体被称为第一代和第二代稀土永磁体。 2:17 type is developed based on 1:5 type.在XNUMX:XNUMX类型的基础上开发了XNUMX:XNUMX类型。 Neodymium magnets dominated the market of rare earth permanent magnets since its inception and then Samarium Cobalt magnets are marginalized seriously due to magnetic performance, complex processing technologies, and costs.自钕钕磁体问世以来,它就一直主导着稀土永磁市场,然后由于磁性能,复杂的加工技术和成本,Sa钴磁体被严重边缘化。 But in fact, sintered Samarium Cobalt magnet is still playing an irreplaceable role in high-temperature and high temperature stability applications which is not possible for但是实际上,Sa钴烧结磁体在高温和高温稳定性应用中仍然扮演着不可替代的角色,这对于 钕磁铁。 The research of high-performance sintered Samarium Cobalt magnets has never stopped, thus complex multistage heating treatment and microstructure control promoted magnetic performance of Samarium Cobalt magnets to an extreme.高性能烧结Sa钴磁体的研究从未停止,因此复杂的多级热处理和微结构控制将d钴磁体的磁性能提升到了极致。 United States Department of Defense demanded that enhance the maximum operating temperature of sintered Samarium Cobalt magnet to the 500 degrees Celsius from 300 degrees Celsius to meet the new applications in aerospace in 1997. In the meanwhile, some higher high-end applications like travelling wave tube and internal device also asked reversible temperature coefficient of sintered Samarium Cobalt magnets should have small enough absolute value.美国国防部要求将烧结mar钴磁铁的最高工作温度从7摄氏度提高到XNUMX摄氏度,以满足XNUMX年在航空航天领域的新应用。与此同时,一些更高端的高端应用,例如行波管并且内部装置还要求烧结Sa钴磁铁的可逆温度系数应具有足够小的绝对值。 Therefore, TbCuXNUMX-type structure因此,TbCuXNUMX型结构 Sm2Co7基磁铁 出现并引起广泛关注。

烧结Sa钴磁铁-主要

烧结钐钴磁体的生产工艺

烧结mar钴磁铁-制造

烧结钐钴磁体磁性能

材料牌号

剩磁

Br

矫顽力

Hcb

内禀矫顽力

Hcj

最多(学期)

能量

产品

(BH)max

居里温度

温度

Tc

最大限度。 歌剧Tem。

Tw

温度Coeff。 的Br温度Coeff。 Hcj的
TkGskA/mKOekAkOekJ/m3MGOe%/℃%/℃
钐钴5可再生能源5 - 16S0.79-0.847.9-8.4620-6607.8-8.3≥1830≥23.0118-13515-17750250-0.035-0.28
可再生能源518S0.84-0.898.4-8.9660-7008.3-8.8≥1830≥23.0135-15117-19750250-0.040-0.28
可再生能源520S0.89-0.93 8.9-9.3684-7328.6-9.2≥1830≥23.0150-16719-21750250-0.045-0.28
可再生能源522S0.92-0.96 9.2-9.6710-7568.9-9.5≥1830≥23.0167-18321-23750250-0.045-0.28
可再生能源524S0.96-1.00 9.6-10.0740-7889.3-9.9≥1830≥23.0183-19923-25750250-0.045-0.28
(SmGd)Co5 LTC-100.62-0.666.2-6.6485-5176.1-6.5≥1830≥23.075-889.5-11.0750300

20-100℃:+0.0156

100-200℃:+0.0087

200-300℃:+0.0007

– 
Sm2(Co,Fe,Cu,Zr)17RE2Co17-24H0.95-1.029.5-10.2692-7648.7-9.6≥1990≥25.0175-19122-24800350-0.025-0.20
RE2Co17-26H1.02-1.0510.2-10.5740-7889.4-10.0≥1990≥25.0191-20724-26800350-0.030-0.20
RE2Co17-28H1.03-1.0810.3-10.8756-8129.5-10.2≥1990≥25.0207-22026-28800350-0.035-0.20
RE2Co17-30H1.08-1.1010.8-11.0788-8359.9-10.5≥1990≥25.0220-24028-30800350-0.035-0.20
RE2Co17-32H1.10-1.1311.0-11.3812-86010.2-10.8≥1990≥25.0230-25529-32800350-0.035-0.20
RE2Co17-220.93-0.979.3-9.7676-7408.5-9.3≥1433≥18.0160-18320-23800300-0.020-0.20
RE2Co17-240.95-1.029.5-10.2692-7648.7-9.6≥1433≥18.0175-19122-24800300-0.025-0.20
RE2Co17-261.02-1.0510.2-10.5748-7969.4-10.0≥1433≥18.0191-20724-26800300-0.030-0.20
RE2Co17-281.03-1.0810.3-10.8756-8129.5-10.2≥1433≥18.0207-22026-28800300-0.035-0.20
RE2Co17-301.08-1.1010.8-11.0788-8359.9-10.5≥1433≥18.0220-24028-30800300-0.035-0.20
RE2Co17-32
1.10-1.1311.0-11.3812-86010.2-10.8≥1433≥18.0230-25529-32800300-0.035-0.20
RE2Co1726M1.02-1.0510.2-10.5676-7808.5-9.8955-143312-18191-20724-26800300-0.035-0.20
RE2Co1728M1.03-1.0810.3-10.8676-7968.5-10.0955-143312-18207-22026-28800300-0.035-0.20
RE2Co1730M1.08-1.1010.8-11.0676-8358.5-10.5955-143312-18220-24028-30800300-0.035-0.20
RE2Co1732M1.10-1.1311.0-11.3676-8528.5-10.7955-143312-18230-25529-32800300-0.035-0.20
RE2Co17-24L0.95-1.029.5-10.2541-7166.8-9.0636-9558-12175-19122-24800250-0.025-0.20
RE2Co17-26L
1.02-1.0510.2-10.5541-7486.8-9.4636-9558-12191-20724-26800250-0.035-0.20
RE2Co17-28L
1.03-1.0810.3-10.8541-7646.8-9.6636-9558-12207-22026-28800250-0.035-0.20
RE2Co17-30L1.08-1.1510.8-11.5541-7966.8-10.0636-9558-12220-24028-30800250-0.035-0.20
RE2Co17-32L1.10-1.1511.0-11.5541-8126.9-10.2636-9558-12230-25529-32800250-0.035-0.20
(Sm,Er)2(Co,Tm)17LTC-160.81-0.858.1-8.5605-6697.6-8.4≥1592≥20117-12714-16840300

-50-20℃:+0.005

20-100℃:-0.008

100-200℃:-0.008

200-300℃:-0.011

 LTC-18 0.85-0.908.5-9.0629-7087.9-8.9≥1592 ≥20127-14316-18840300
 LTC-200.90-0.949.0-9.4661-7328.3-9.2≥1592 ≥20143-15918-20840300
 LTC-220.94-0.979.4-9.7685-7408.6-9.3≥1592 ≥20159-17520-22840300
  • 上表中磁体的磁性能及物理性能基于室温测量。
  • 磁体最高工作温度同时受长径比,涂层厚度和其他环境因素影响。

烧结钐钴磁体物理性质

参数 单位 钐钴5 Sm2Co17
密度/ρ g/cm3 8.1-8.5 8.3-8.5
维氏硬度 HV 450-500 500-600
抗压强度 MPa 420-680 700-830
电阻率 Ω·cm (5-6)x10-5 (8-9)x10-5
热膨胀系数 10-6/K

C⊥:13

C∥:6

C⊥:11

C∥:8

不同磁性材料之间的性能差异

材料

(BH)max

MGOe

Hcj

kOe

剩磁温度系数

%/℃

最高工作温度

抗腐蚀性能
钐钴516-2515-25-0.05200-250
Sm2Co1722-326-30-0.03250-350
Nd2Fe14B26-5212-33-0.1180-230
铁氧体3.0-4.53.0-4.5-0.19200-300
铝镍钴5-101.0-1.8-0.03450-500优秀

备注:

  • 实际上,由于自身脆性,烧结钐钴磁体并不适合作为结构件。
  • 钐钴5 相比于Sm2Co17 更容易加工。
  • 采购不充磁钐钴磁体的客户自身应配备合适的充磁设备以确保磁体能够饱和充磁。
  • 胜势登也可提供有镀层的钐钴磁体以应对恶劣工作条件。